Nickel-Iron-Chromium-Molybdenum N06002
Chemical Compostion:
| Material | Ni | Cr | Iron | Mn | C | Si max | S max | Mo | P max | W 钨 | Co |
| N06002 | remainder | 20.5-23.5 | 17.0-20.0 | 1.00 | 0.05-0.15 | 1.00 | 0.030 | 8.0-10.0 | 0.04 | 0.20-1.0 | 0.5-2.5 |
Mechanical Properties:
| Material | Tensile Strength,Min PSI (MPa) | Yield Strength (0.2% offset) Min(Mpa) | Elongation in 2 in. or 50mm or 4D,Min.,% |
| N06002 | 100000(690) | 40000(276) | 35 |
Standards:
| Material | Seamless Tubing &/or Pipe | Welded Tubing | Welded Pipe | Buttweld fitting | Plate/Sheet/Strip | Bar Forging and Forging stock |
| N06002 | SB-622 | SB-626 | SB-619 | SB-366 | SB-435 | SB-572 |
Hastelloy X is a nickel-chromium-iron-molybdenum superalloy with outstanding high temperature strength, oxidation resistance, and
fabricability. Alloy X’s oxidation resistance is excellent up to 2200°
F. This nickel steel alloy has also been found to be exceptionally
resistant to stress-corrosion cracking in petrochemical applications.
Matrix stiffening provided by the molybdenum content results in high
strength in a solid-solution alloy having good fabrication
characteristics. Although this nickel alloy is primarily noted for heat
and oxidation resistance it also has good resistance to chloride
stress-corrosion cracking, carburization, and excellent resistance to
reducing or carburizing atmospheres. Two common conditions that often
lead to early failure in high temperature alloys, carburization and
nitriding, Hastelloy X resists.